Available online 17 November 2023

Manufacturing techniques affect fatigue strength.

Polishing protocol provokes phase transition of zirconia.

Printing layers parallel to the tensile surface achieves the best fatigue strength.

The aim of the study was to evaluate the influence of surface polishing and printing layer orientation on the fatigue behaviour of 3 mol% yttria-stabilized zirconia (3Y-TZP) by stereolithography (SLA) in comparison with subtractive manufacturing.

60 experimental zirconia bar-shaped specimens were 3D-printed (P) via SLA, and 30 specimens were milled (M) from commercial zirconia block (Lava™ Frame, 3 M ESPE AG). All specimens had the same dimensions (1 mm × 1 mm x 12 mm) after sintering. The 3D-printed specimens were randomly divided according to printing orientations: parallel or perpendicular to the tensile surface in the fatigue test. The specimens were subsequently submitted to two surface finishing protocols (n = 15/gr): unpolished or polished. Their phase compositions were analysed by X-ray diffraction. The fatigue behaviour was evaluated by a stepwise approach.

The milled and both 3D-printed groups showed similar phase compositions for the as-sintered condition. Considerable amounts of rhombohedral phase were detected after polishing. Milled unpolished samples presented significantly higher fatigue strength than 3D-printed unpolished samples. Polishing did not improve the fatigue strength for milled zirconia but was advantageous for the 3D-printed specimens. 3D-printed specimens with parallel printing-layer orientation were significantly stronger than specimens with perpendicular layers regardless of surface finishing.

The manufacturing techniques had a significant influence on the fatigue strength of 3Y-TZP, but not on the phase compositions of the surface. The polishing protocol showed different effects on 3Y-TZP fatigue strength and induced phase transition of the 3Y-TZP from Tetragonal to Rhombohedral. The best fatigue strength was achieved through milling using an unpolished surface and SLA-printed layers that were parallel to the tensile surface, followed by polishing.

3D printing

Vat photopolymerization

Stereolithography

Zirconia

Fatigue

X-ray diffraction

© 2023 The Author(s). Published by Elsevier Inc. on behalf of The Academy of Dental Materials.